A polypropylene resin composition affords a molded article good in rigidity, impact resistance, and tensile elongation at break. This composition contains 75-98 wt % of a propylene-based material (A) and 2-25 wt % of a propylene-ethylene random copolymer (B). Material (A) contains 50-100 wt % of a polymeric material (A-1) produced by multistage polymerization and composed of a propylene homopolymer component (i) and a propylene-ethylene random copolymer component (ii), and 0-50 wt % of a propylene homopolymer (A-2). The content of (i) in material (A-1) is 55-90 wt %, and the content of (ii) is 10-45 wt %, (ii) in material (A-1) contains >40 wt % but ≦̸80 wt % of ethylene units and ≧20 wt % but <60 wt % of propylene units, and the content of (ii) in material (A) is 5-35 wt %. Copolymer (B) contains 88-95 wt % of propylene units and 5-12 wt % of ethylene units and has an MFR of 0.5-10 g/10 minutes measured at 230° C. and a load of 2.16 kgf. |