摘要

Provided is a method for fabricating a stepped forged material that can realize a uniform microscopic structure in both the large diameter flange portion and the small diameter shaft portion. This method for fabricating a stepped forged material comprises the following steps: a step for obtaining a primary forged material in which an austenite stainless steel billet is heated to 1000-1080° C., and, without any further heating, the material is forged by means of reciprocal forging into a round rod having along the entire length thereof a forging ratio of 1.5 or greater; a step for obtaining a secondary forged material, that forms the large diameter flange portion and the small diameter shaft portion, in which without reheating, the small diameter shaft portion is formed by means of reciprocal forging at a temperature where the surface temperature of the primary forged material never falls more than 200° C. lower than the abovementioned material heating temperature and the forging is completed before the surface temperature of the final forged portion falls more than 300° C. lower than the abovementioned heating temperature; and a step for performing a solution heat treatment in which the secondary forged material is heated to 1040-1100° C. for 30 minutes or longer.

主权项

1. A method for producing a stepped forged material, comprising the steps of:
obtaining a primary forged material, wherein an austenite stainless steel billet for forging is heated to 1000-1080° C., and, without any further heating, the material is forged into a round rod having a forging ratio of 1.5 or greater along the entire length of the material by means of reciprocal forging of repeating a forging operation in which the material is delivered from one end to the other end in the axial direction with respect to a forging apparatus and thereafter delivered in the opposite direction; obtaining a secondary forged material formed to have a large diameter flange portion and a small diameter shaft portion, wherein without reheating, forging is started at a temperature before a surface temperature of the primary forged material falls more than 200° C. lower than the material heating temperature, and the small diameter shaft portion is formed by means of reciprocal forging of repeating a forging operation in which the primary forged material is delivered from one end in the axial direction to a predetermined position with respect to the forging apparatus and thereafter delivered in the opposite direction, and the forging is completed before a surface temperature of a final forged portion falls more than 300° C. lower than the material heating temperature; and performing a solution heat treatment, wherein the secondary forged material is heated to 1040-1100° C. for 30 minutes or longer.