发明名称 |
Heat Treatment for Reducing Distortion |
摘要 |
Methods of processing an aluminum alloy component are disclosed. The method may include solution heat treating the component at a solution heat treatment (SHT) temperature of 500° C. to 535° C., quenching the component in a liquid quenching medium having a temperature of 75° C. to 95° C., and artificially aging the component at an artificial aging (AA) temperature of 200° C. to 250° C. to a yield strength of at least 200 MPa. The component may be a 6XXX series aluminum alloy, which may be (or have been) progressively stamped. The component may be artificially aged to an r/t ratio of less than 0.3. The liquid quenching medium may be water and may have a temperature of 82° C. to 88° C. The method may further include joining the aluminum alloy component to a second component with a self-piercing rivet. The disclosed methods may reduce distortion in the component while maintaining high strength and bendability. |
申请公布号 |
US2017044650(A1) |
申请公布日期 |
2017.02.16 |
申请号 |
US201514822379 |
申请日期 |
2015.08.10 |
申请人 |
Ford Motor Company |
发明人 |
HARRISON Nia R.;DHAR Suranjeeta;WHITE-JOHNSON Patrice |
分类号 |
C22F1/057;C22F1/05;C22F1/043;C22F1/00;B62D65/00;C22C21/08;C22C21/14;C22C21/16;C22C21/18;B62D29/00;C22F1/047;C22C21/02 |
主分类号 |
C22F1/057 |
代理机构 |
|
代理人 |
|
主权项 |
1. A method of processing an aluminum alloy component, comprising:
solution heat treating the component at a solution heat treatment (SHT) temperature of 500° C. to 535° C.; quenching the component in a liquid quenching medium having a temperature of 75° C. to 95° C.; and artificially aging the component at an artificial aging (AA) temperature of 200° C. to 250° C. to a yield strength of at least 200 MPa. |
地址 |
Dearborn MI US |