发明名称 |
METHOD FOR PRODUCING PLATINUM GROUP ALLOY |
摘要 |
Provided is a method for producing a platinum group-based alloy capable of producing a sound molten ingot of a platinum group-based alloy in a large amount. The method for producing a platinum group-based alloy includes a molten ingot production step of a continuous casting system using a plasma arc melting furnace configured to form a plasma arc column between an electrode torch which is arranged in an upper part of a vacuum chamber and a water cooled copper crucible which is arranged in a lower part of the chamber and has a cavity having a sectional area S1, the molten ingot production step including: inserting and melting an end part of a raw material bar including a platinum group-based alloy in the plasma arc column to cause the raw material bar to fall in drops on a base material in the water cooled copper crucible, to thereby form a molten pool; and solidifying a bottom part of the molten pool while maintaining a constant liquid level height of the molten pool by pulling down the base material, the molten ingot having a horizontal sectional area S (mm2) and a length L (mm) satisfying the following relationship: S1≧S>500, L>4√(S/π), an internal pressure of the chamber during melting being 0.8 atm or more, a pulling down speed of the base material being 10 mm/min or less. |
申请公布号 |
US2017043393(A1) |
申请公布日期 |
2017.02.16 |
申请号 |
US201515307138 |
申请日期 |
2015.03.27 |
申请人 |
ISHIFUKU Metal Industry Co., Ltd. |
发明人 |
DOI Yoshinori;KON Daisuke |
分类号 |
B22D11/18;B22D11/041 |
主分类号 |
B22D11/18 |
代理机构 |
|
代理人 |
|
主权项 |
1. A method for producing a platinum group-based alloy, the method comprising a molten ingot production step of a continuous casting system using a plasma arc melting furnace configured to form a plasma arc column between an electrode torch which is arranged in an upper part of a vacuum chamber and a water cooled copper crucible which is arranged in a lower part of the chamber and has a cavity having a sectional area S1,
the molten ingot production step comprising: inserting and melting an end part of a raw material bar comprising a platinum group-based alloy in the plasma arc column to cause the raw material bar to fall in drops on a base material in the water cooled copper crucible, to thereby form a molten pool; and solidifying a bottom part of the molten pool while maintaining a constant liquid level height of the molten pool by pulling down the base material, the molten ingot having a horizontal sectional area S and a length L satisfying the following relationship:
S1≧S>500 (mm2),L>4√(S/π) (mm), an internal pressure of the chamber during melting being 0.8 atm or more, a pulling down speed of the base material being 10 mm/min or less. |