发明名称 |
Glass fiber structure designed to reinforce bonded abrasive articles |
摘要 |
The invention relates to a structure based on glass fiber coated with a resin composition designed to reinforce bonded abrasive articles, the resin composition including the following constituents in the proportions indicated, expressed in percentage by weight of solid matter:
75 to 98% of a mixture of at least one novolac having a glass transition temperature lower than or equal to 60° C. and at least one novolac having a glass transition temperature above 60° C.,0.5 to 10% of at least one wax,0 to 3.5% of at least one plasticizing agent. |
申请公布号 |
US9556356(B2) |
申请公布日期 |
2017.01.31 |
申请号 |
US201313939271 |
申请日期 |
2013.07.11 |
申请人 |
SAINT-GOBAIN ADFORS |
发明人 |
Arnaud Alix;Espiard Philippe;Ceugniet Claire |
分类号 |
C09K3/14;C09D161/06;B24D3/34;C08L61/06;C08L23/06;C08L91/06 |
主分类号 |
C09K3/14 |
代理机构 |
Oblon, McClelland, Maier & Neustadt, L.L.P. |
代理人 |
Oblon, McClelland, Maier & Neustadt, L.L.P. |
主权项 |
1. A resin composition, comprising the following, expressed in percentage by weight
25 to 55% of at least one first novolac having a glass transition temperature lower than or equal to 60° C., 10 to 30% of at least one second novolac having a glass transition temperature above 60° C., 0.5 to 6.5% of at least one wax, 0 to 2.5% of at least one plasticizing agent, 25 to 45% of at least one alcohol, 0 to 15% of water, wherein the resin composition does not comprise a crosslinking agent. |