| 摘要 |
The present invention provides dense silica particles with reduced metal impurities. Specifically, the present invention provides a colloidal silica produced by using an alkyl silicate as a starting material, wherein, with respect to a sample prepared by adding, as an internal standard, 1 wt. % of polydimethylsilane to a dried product of the colloidal silica, a peak area value calculated using a formula of a colloidal silica peak area/a polydimethylsilane peak area is 15 or less, the peak areas being determined by an obtained solid-state 29Si-CP/MAS-NMR spectrum. The present invention further provides a method for producing the colloidal silica. |
| 主权项 |
1. A method for producing a colloidal silica, comprising the steps of:
1) preparing a mother liquid comprising an alkali catalyst and water; 2) separately preparing a hydrolyzed liquid by hydrolyzing tetramethyl orthosilicate in the absence of a catalyst; and 3) after steps 1) and 2), adding, to the mother liquid, the hydrolyzed liquid to produce the colloidal silica wherein the hydrolyzed liquid is added to the mother liquid at a rate of not less than 0.7 g of silica/hour/kg of mother liquid and not greater than 41 g of silica/hour/kg of mother liquid; and
the colloidal silica satisfies the following conditions: a) with respect to a sample prepared by adding, as an internal standard, 1 wt. % of polydimethylsilane to a dried product of the colloidal silica, a peak area value calculated using a formula of a colloidal silica peak area/a polydimethylsilane peak area is 15 or less, the peak areas being determined by measuring a solid-state 29Si-CP/MAS-NMR spectrum of the dried product; b) each amount of
i) sodium,ii) an alkaline earth metal selected from calcium and magnesium; andiii) a heavy metal selected from iron, titanium, nickel, chromium, copper, zinc, lead, silver, manganese, and cobalt, contained in the colloidal silica is 1 wt. ppm or less. |