发明名称 |
STRUCTURAL ALUMINUM ALLOY PLATE AND METHOD OF PRODUCING THE SAME |
摘要 |
A structural aluminum alloy plate includes 7.0% to 12.0% by mass of Zn, 1.5% to 4.5% by mass of Mg, 1.0% to 3.0% by mass of Cu, 0.05% to 0.30% by mass of Zr, 0.005% to 0.5% by mass of Ti, 0.5% or less by mass of Si, 0.5% or less by mass of Fe, 0.3% or less by mass of Mn, 0.3% or less by mass of Cr, and the balance that includes aluminum and inevitable impurities. A method of producing the structural aluminum alloy plate is also provided. |
申请公布号 |
US2017016102(A1) |
申请公布日期 |
2017.01.19 |
申请号 |
US201415123896 |
申请日期 |
2014.11.13 |
申请人 |
UACJ Corporation |
发明人 |
Nakanishi Hidetaka;Norikane Kazushige;Asano Mineo |
分类号 |
C22F1/053;C22C21/10;C22F1/00 |
主分类号 |
C22F1/053 |
代理机构 |
|
代理人 |
|
主权项 |
1. A structural aluminum alloy plate comprising:
7.0% to 12.0% by mass of Zn; 1.5% to 4.5% by mass of Mg; 1.0% to 3.0% by mass of Cu; 0.05% to 0.30% by mass of Zr; 0.005% to 0.5% by mass of Ti, 0.5% or less by mass of Si; 0.5% or less by mass of Fe; 0.3% or less by mass of Mn; 0.3% or less by mass of Cr; and the balance being aluminum and inevitable impurities, wherein the structural aluminum alloy plate comprises a texture in which
an orientation density of at least one crystal orientation of three crystal orientations, which are Brass orientation, S orientation, and Copper orientation, is 20 or more in random ratio, andorientation densities of all of five crystal orientations, which are Cube orientation, CR orientation, Goss orientation, RW orientation, and P orientation, are 10 or less in random ratio, and wherein the structural aluminum alloy plate comprises
a tensile strength of 660 MPa or more and a 0.2% yield strength of 600 MPa or more in each of a 0-degree direction and a 90-degree direction relative to a longitudinal rolling direction;an elongation at break in each of the 0-degree direction and the 90-degree direction is 70% or more of an elongation at break in a 45-degree direction relative to the longitudinal rolling direction;a tensile strength in the 45-degree direction is 80% or more of the tensile strength in the 0-degree direction, and a 0.2% yield strength in the 45-degree direction is 80% or more of the 0.2% yield strength in the 0-degree direction; andthe elongation at break in the 45-degree direction is 12% or more. |
地址 |
Tokyo JP |