Method of making oil-in-water emulsified composition using corona-core microgel emulsifying agent

摘要

The present invention provides a corona-core microgel emulsifying agent composed of a copolymer obtained by polymerizing polyethylene oxide macromonomers, hydrophobic monomers, and cross-linking monomers under specific conditions as well as an oil-in-water emulsified composition characteristically using said emulsifying agent for emulsification.;The object of the present invention is to provide a new corona-core microgel emulsifying agent to be used to prepare an oil-in-water emulsified composition that manifests superior emulsification stability, stability over time, and low skin irritation, and is free of stickiness at the time of application, manifests dewy freshness, is free of powdery sensation and/or squeakiness, and is superior in durability of fragrance, as well as an oil-in-water emulsified composition emulsified with said emulsifying agent.

主权项

1. A method of preparing an oil-in-water Pickering emulsion comprising
a corona-core microgel emulsifying agent in an amount of 0.1-3 wt % of the total amount of the oil-in-water Pickering emulsion, an oil phase ingredient in an amount of 10-80 wt % of the total amount of the oil-in-water Pickering emulsion, and a water phase ingredient,wherein the corona-core microgel emulsifying agent is composed of a copolymer obtained by polymerizing polyethylene oxide macromononiers of the following formula (1), hydrophobic monomers of the following formula (2), and cross-linking monomers of the following formula (3) under the following conditions (A) and (B):
(A) a mole ratio of a feed mole amount of said polyethylene oxide macromonomers/a feed mole amount of the hydrophobic monomers is 1:10-1:250; and (B) a feed amount of said cross-linking monomers is 0.1-1.5 wt % relative to a feed amount of said hydrophobic monomers; R1 denotes an alkyl having 1-3 carbon atoms, n is an integer 8-200, and X denotes H or R2 denotes an alkyl having 1-3 carbon atoms, and R3 denotes an alkyl having 1-12 carbon atoms; and R4 and R5 each independently denote an alkyl having 1-3 carbon atoms, and m is a number 0-2; and wherein a core part is cross-linked with cross-linking monomers to prepare the microgel by using polymer fine particle polymerization method; the method comprising the steps of: mixing and dispersing the corona-core microgel emulsifying agent in water or the water phase ingredient to form a dispersion; adding the oil phase ingredient to the dispersion to form a mixture; and emulsifying the mixture by stirring and applying shearing force.