Aluminum alloy foil for electrode collectors and production method therefor

摘要

An object of the present invention is to provide an aluminum alloy foil for an electrode current collector, the foil having a high strength after the drying step while keeping a high electrical conductivity. Disclosed is a method for manufacturing an aluminum alloy foil for electrode current collector, including: maintaining an aluminum alloy ingot comprising 0.1 to 0.5% of Fe, 0.01 to 0.3% of Si, 0.01 to 0.2% of Cu, 0.01% or less of Mn, with the rest being Al and unavoidable impurities, at 550 to 620° C. for 1 to 20 hours, and subjecting the resulting ingot under a hot rolling with a starting temperature of 500° C. or higher and an end-point temperature of 255 to 300° C.

主权项

1. An aluminum alloy foil for electrode current collector, manufactured by the process including:
maintaining an aluminum alloy ingot at 550 to 620° C. for 1 to 20 hours, wherein the aluminum alloy ingot comprises 0.1 to 0.5 mass % (hereinafter referred to as %) of Fe, 0.01 to 0.3% of Si, 0.01 to 0.2% of Cu, 0.01% or less of Mn, with the rest consisting of Al and unavoidable impurities; and subjecting the resulting ingot under a hot rolling with a starting temperature of 500° C. or higher and an end-point temperature of 255 to 300° C., wherein tensile strength of the aluminum alloy foil is 220 MPa or higher, 0.2% yield strength of the aluminum alloy foil is 180 MPa or higher, electrical conductivity of the aluminum alloy foil is 58% International Annealed Copper Standard (IACS) or higher, a solid solution of Fe formed in the aluminum alloy foil is 100 ppm or higher, a solid solution of Si formed in the aluminum alloy foil is 80 to 1800 ppm, and a solid solution of Cu formed in the aluminum alloy foil is 80 to 1500 ppm.