| 摘要 |
A cold-rolled steel plate having favorable heat spot resistance and favorable antiwear performance is provided. The cold-rolled steel plate has a chemical composition containing C from 0.03 to 0.12%, Si from 0 to 1.0% (including a case where Si is not added), Mn from 0.2 to 0.8%, P at 0.03% or less (excluding a case where P is not added), S at 0.03% or less (excluding a case where S is not added), Ti from 0.04 to 0.3%, and A1 at 0.05% or less (excluding a case where A1 is not added). A residue is formed of Fe and unavoidable impurities. Each element satisfies a relationship of 5 * C% - Si% + Mn% - 1.5 * Al% < 1 within the aforementioned range of the corresponding content. An average diameter of particles of a Ti-based carbide is from 20 to 100 nm. In this way, the Ti-based carbide is dispersed finely and uniformly, thereby enhancing heat spot resistance and antiwear performance. |