| 摘要 |
A process for enhancing the gas barrier properties of a composite laminate material whilst maintaining adequate bond strength, in which a gas barrier coating comprising a clay dispersion and a polymer solution or dispersion is positioned between two flexible plastics films using an adhesive, wherein a coating is applied to a first flexible polymer film at a coating weight (D), an adhesive is applied to either or both of the coated side of the first film or to a second polymer film and adhering the first and second films together to provide a material in which: (A/B). (C/D)>200, and in which: A/B>75; C>1.0; and D<1.5; wherein: A=Oxygen Transmission Rate for the laminate at 23 0C and 50% RH without the coating; B=Oxygen Transmission Rate for the laminate at 23 0C and 50% RH with the coating; C=Bond Strength in N/15 mm after the adhesive has fully cured; D=Coating Weight in g/m2 (dry). |