A method of manufacturing fine grain titanium alloy sheets that is suitable for superplastic forming (SPF) is disclosed. In one embodiment, a high strength titanium alloy comprising: Al: about 4.5% to about 5.5%, V: about 3.0% to about 5.0%, Mo: about 0.3% to about 1.8%, Fe: about 0.2% to about 0.8%, O: about 0.12% to about 0.25% with balance titanium is forged and hot rolled to sheet bar, which is then fast-cooled from a temperature higher than beta transus. According to this embodiment, the sheet bar is heated between about 1400° F. to about 1550° F. and rolled to intermediate gage. After reheating to a temperature from about 1400° F. to about 1550° F., hot rolling is performed in a direction perpendicular to the previous rolling direction to minimize anisotropy of mechanical properties. The sheets are then annealed at a temperature between about 1300° F. to about 1550° F. followed by grinding and pickling. |