发明名称 |
DULL POLYAMIDE 56 FIBER AND METHOD FOR MANUFACTURING THE SAME |
摘要 |
A method for manufacturing a dull polyamide 56 fiber includes steps as follows. Bright polyamide 56 chips are provided. A viscosity adjusting step is provided, wherein a relative viscosity in sulfuric acid of the bright polyamide 56 chips is adjusted to a range of 2.90 to 3.00. A moisture adjusting step is provided, wherein a moisture content of the bright polyamide 56 chips is adjusted to a range of 350 to 550 ppm. A spinning step is provided, which includes providing dull polyamide 6 chips and a blending step. The dull polyamide 6 chips include TiO2. In the blending step, the dull polyamide 6 chips and the bright polyamide 56 chips dealt with the viscosity adjusting step and the moisture adjusting step are melted and blended, and then spun at a temperature ranging from 275° C. to 285° C., thus the dull polyamide 56 fiber is obtained. |
申请公布号 |
US2016176094(A1) |
申请公布日期 |
2016.06.23 |
申请号 |
US201514829647 |
申请日期 |
2015.08.19 |
申请人 |
CHAIN YARN CO., LTD. |
发明人 |
CHEN Yen-Hsiao;CHAO Tsung-Hsien;CHEN Shih-Yang;HSIEH I-Chen |
分类号 |
B29C47/00 |
主分类号 |
B29C47/00 |
代理机构 |
|
代理人 |
|
主权项 |
1. A method for manufacturing a dull polyamide 56 fiber, comprising:
providing a plurality of bright polyamide 56 chips; providing a viscosity adjusting step, wherein a relative viscosity in sulfuric acid of the bright polyamide 56 chips is adjusted to a range of 2.90 to 3,00; providing a moisture adjusting step, wherein a moisture content of the bright polyamide 56 chips is adjusted to a range of 350 ppm to 550 ppm; and providing a spinning step, comprising:
providing a plurality of dull polyamide 6 chips, wherein the dull polyamide 6 chips comprise titanium dioxide (TiO2);andproviding a blending step, wherein the dull polyamide 6 chips and the bright polyamide 56 chips dealt with the viscosity adjusting step and the moisture adjusting step are melted and blended, and then spun at a temperature ranging from 275° C. to 285° C., thus the dull polyamide 56 fiber is obtained. |