A leucite glass-ceramic is prepared from a glass comprising: about 66.8 to about 71.9 mol % of SiO2, about 8.5 to about 10.6 mol % of Al2O3, about 9.5 to about 12.8 mol % of K2O, about 0.5 to about 4.0 mol % of CaO, about 0 to about 3.0 mol % of TiO2, about 1.8 to about 4.0 mol % of Na2O, about 0.1 to about 6.0 mol % of Li2O, about 0 to about 1.0 mol % of MgO, about 0 to about 3.0 mol % of Nb2O5, and about 0 to about 3.0 mol % of B2O3. The leucite glass-ceramic is prepared by subjecting the glass components to a nucleation heat treatment, followed by a growth heat treatment. The leucite glass-ceramic may be used in the fabrication of a Dental restoration using various processes, and may be used in the construction of Dental restorations such as ceramic Dental inlays, crowns, veneers, bridges, veneering materials for zirconium oxide restoration substrates, alumina oxide restoration substrates, or metal restoration substrates. |
| 主权项 |
1. A leucite glass-ceramic prepared from a glass comprising: about 66.8 to about 71.9 mol % of Si02, about 8.5 to about 10.6 mol % of Al203, about 9.5 to about 12.8 mol % of K20, about 0.5 to about 4.0 mol % of CaO, about 0 to about 3.0 mol % of Ti02, about 1.8 to about 4.0 mol % of Na20, about 0.1 to about 6.0 mol % of Li20, about 0 to about 1.0 mol % of MgO, about 0 to about 3.0 mol % of Nb2O5, and about 0 to about 3.0 mol % of B203. |