COATING COMPOSITION, COATING FILM FORMATION METHOD AND TRANSPARENT COATING FILM |
摘要 |
PROBLEM TO BE SOLVED: To provide: a coating composition capable of forming a coating film having high transparency, oxygen blocking property and weather resistance for coating the surface of a reinforced concrete structure; a method for forming a coating film by using the coating composition; and a transparent coating film formed by the coating composition.SOLUTION: There is provided a coating composition used for forming a transparent coating film for coating the surface of a reinforced concrete structure, wherein the coating composition comprises an epoxy resin (a) having no aromatic ring, a modified aliphatic amine compound (b) and flat-shaped inorganic particles (c), the inorganic particles (c) are at least one of mica and glass flakes, the average aspect ratio of the inorganic particles (c) is 20 to 1000, the oxygen permeability of a coating film having a film thickness of 1000 μm which is formed using the coating composition and then cured is 0.05 mg/(cmday) or less and the hiding ratio of a coating film having a film thickness of 300 μm which is formed using the coating composition and then cured is 45% or less.SELECTED DRAWING: None |
申请公布号 |
JP2016079193(A) |
申请公布日期 |
2016.05.16 |
申请号 |
JP20140208298 |
申请日期 |
2014.10.09 |
申请人 |
NIPPON PAINT CO LTD;PUBLIC WORKS RESEARCH INSTITUTE |
发明人 |
HOSHINO MASAYA;MORIMOTO TAKAO;KAWASHIMA YUJI;MIYATA ATSUSHI;NISHIZAKI ITARU;SASAKI TSUYOSHI |
分类号 |
C09D163/00;B05D1/28;B05D7/00;C09D7/12;C09D133/14 |
主分类号 |
C09D163/00 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|