POLYMER PROPPANT AND METHOD FOR PRODUCING SAME

摘要

The polymer proppant and method for producing the same relate to oil and gas production technology using materials of high-molecular weight compounds with higher requirements for physical and mechanical properties. The proppant is used as propping granules utilized in the oil and gas production by a method of hydraulic fracturing of formation. The technical result achieved by implementation of the present invention is an increase in thermal strength of the proppant whose material provides a compressive strength of at least 150 MPa at a temperature of not less than 100° C. The polymer proppant represents microspheres of metathesis-radically cross-linked mixture of oligocyclopentadienes.

主权项

1. A method for producing a proppant, including obtaining a mixture of oligocyclopentadienes by heating dicyclopentadiene to a temperature of 150-220° C. and holding at this temperature for 15-360 minutes, cooling the mixture down to 20-50° C., sequentially adding the following components to the resulting mixture of oligocyclopentadienes: at least one of polymer stabilizers as which the following compounds are used: tetrakis[methylene(3,5-di-tert-butyl-4-hydroxyhydrocinnamate)]methane, 2,6-di-tert-butyl-4-(dimethylamino)phenol, 1,3,5-trimethyl-2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)benzene, tris(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)isocyanurate, 3,5-di-tert-butyl-4-hydroxyanisole, 4,4′-methylenebis(2,6-di-tert-butylphenol), diphenylamine, para-di-tert-butylphenylenediamine, N,N′-diphenyl-1,4-phenylenediamine, tris(2,4-di-tert-butylphenyl)phosphite, tris(nonylphenyl)phosphite, bis(2,2,6,6-tetramethyl-4-piperidinyl)sebacate, bis(1-octyloxy-2,2,6,6-tetramethyl-4-piperidinyl)sebacate, bis(1-methyl-2,2,6,6-tetramethyl-4-piperidinyl)sebacate, 2-tert-butyl-6-(5-chloro-2H-benzotriazol-2-yl)-4-methylphenol, 2-(2H-benzotriazol-2-yl)-4,6-bis(1-methyl-1-phenyl)phenol; at least one of radical initiators as which the following compounds or mixtures thereof are used: di-tert-butyl peroxide, dicumyl peroxide, 2,3-dimethyl-2,3-diphenylbutane, triphenylmethane; and a catalyst as which a compound of the following general formula is used: wherein a substituent L is selected from the group: wherein the components of the polymer matrix are present in the following amounts, wt. %:
the antioxidants polymer stabilizers 0.1-3;the radical initiators 0.1-4;the catalyst 0.001-0.02;the mixture of oligocyclopentadienes being the balance, the resulting polymer matrix is held at a temperature of 20-50° C. for 1-40 minutes, and thereafter is introduced as a laminar flow into water preheated to a temperature not lower than that of the matrix, said water containing a surfactant as which cetyltrimethylammonium chloride or sodium dodecyl sulfate or ammonium lauryl sulfate or sodium lauryl sarcosinate or octenidine hydrochloride or benzalkonium chloride is used; while constantly stirring, the water is heated up to 50-100° C., while still continuing stirring for 1-60 minutes; microspheres formed are separated from the water, are heated in an inert gas atmosphere to a temperature of 150-340° C. and are held under said atmosphere at this temperature for 1-360 minutes.