| 摘要 |
Provided are a high-strength hot-rolled steel sheet having a tensile strength of 980 MPa or more and excellent in terms of bending workability and a method for manufacturing the steel sheet. A high-strength hot-rolled steel sheet having a tensile strength TS of 980 MPa or more is manufactured by controlling the steel sheet to have a chemical composition containing C: more than 0.1% and 0.2% or less, Si: 0.5% or more and 3.0% or less, Mn: 1.0% or more and 3.5% or less, P: 0.05% or less, S: 0.004% or less, Al: 0.10% or less, N: 0.008% or less, Ti: 0.05% or more and 0.15% or less, V: more than 0.10% and 0.30% or less, and the balance being Fe and inevitable impurities. Surface regions have a microstructure including mainly a ferrite phase, and an inner region has a microstructure including mainly a bainite phase. The proportions of the surface regions in the thickness direction of the steel sheet are 1.0% or more and 5.0% or less of the whole thickness respectively from the upper and lower surfaces of the steel sheet. |