The invention relates to a method and a device for producing a multifilament thread from a polyamide melt. In this case, first of all freshly extruded filaments are cooled and combined to form a thread. In order, in addition to low boil-off shrinkage, to achieve high strength, the thread is taken off at a take-off rate in the range from 3600 m/min to 4600 m/min, preferably from 4000 m/min to 4400 m/min, by a first godet group having unheated guide casings. Subsequently, the thread is fully drawn between the godet group having unheated guide casings and a second godet group having heated guide casings. After drawing, the thread is heated to a thread temperature in the range from 140°C to 200°C under tension at the guide casings of the second godet group and relaxed. After relaxing, the thread runs in a contact-free manner through at least one free cooling section between the second godet group and a third godet group having unheated guide casings. |