METHOD FOR PRODUCING GALVANIZED STEEL SHEET FOR HOT STAMPING, ALLOYED HOT-DIPPED GALVANIZED STEEL SHEET FOR HOT STAMPING AND METHOD FOR PRODUCING SAME, AND HOT STAMPED COMPONENT

摘要

Provided is a method for producing a plated steel sheet with high Si content for hot stamping, which is capable of suppressing the generation of unplated portions, while maintaining high bonding strength in a welded part in cases where a galvanized steel sheet containing a large amount of Si, namely, 0.7% or more of Si is used for hot stamping applications. In this production method, a hot-rolled pickled steel sheet or cold-rolled steel sheet containing 0.10-0.5% by mass of C, 0.7-2.5% by mass of Si, 1.0-3% by mass of Mn, and 0.01-0.5% by mass of Al is annealed in a reducing atmosphere and then plated, thereby producing a galvanized steel sheet for hot stamping. This method for producing a galvanized steel sheet for hot stamping is characterized in that the annealing is carried out within the range of 500 to 700°C for 30 to 270 seconds.