摘要 |
离心铸造高硼高速钢复合轧辊及其制备方法,属于复合铸造技术领域。复合轧辊的辊身外层采用高硼高速钢,辊芯内层采用球墨铸铁,中间过渡层采用高强度低硅铸铁。外层化学成分及质量分数:0.65~0.95%C,1.5~1.8%B,3.0~3.5%Mo,1.2~1.5%W,1.0~1.2%V,6.0~6.5%Cr,1.5~1.8%Al,0.04~0.08%Y,0.04~0.08%Mg,0.12~0.25%Nb,0.08~0.15%N,0.05~0.12%Na,0.5~1.5%Si,Mn<0.8%,S<0.04%,P<0.04%,余量Fe。复合轧辊经淬火和回火处理后,具有良好的力学性能和优异的耐磨性。 |
主权项 |
离心铸造高硼高速钢复合轧辊,其特征在于,复合轧辊的辊身外层采用高硼高速钢,辊芯内层采用球墨铸铁,中间过渡层采用高强度低硅铸铁;外层高硼高速钢的化学成分及质量分数为:0.65~0.95%C,1.5~1.8%B,3.0~3.5%Mo,1.2~1.5%W,1.0~1.2%V,6.0~6.5%Cr,1.5~1.8%Al,0.04~0.08%Y,0.04~0.08%Mg,0.12~0.25%Nb,0.08~0.15%N,0.05~0.12%Na,0.5~1.5%Si,Mn<0.8%,S<0.04%,P<0.04%,余量Fe;内层球墨铸铁的化学成分及质量分数为:3.1~3.4%C,1.8~2.2%Si,0.4~0.6%Mn,0.3~0.4%Ni,0.05~0.20%Cr,0.15~0.25%Mo,0.04~0.06%Mg,0.02~0.05%Ce,0.01~0.03%Sb,0.03~0.05%Ca,0.03~0.05%Ba,P<0.08%,S<0.03%,余量Fe;中间过渡层高强度低硅铸铁的化学成分及质量分数为:3.1~3.4%C,0.8~1.1%Si,0.3~0.5%Mn,0.1~0.2%Mo,0.10~0.15%V,0.02~0.05%N,P<0.08%,S<0.03%,0.03~0.06%Y,余量Fe。 |