Thin joint member producing method and pair of thin joint members |
摘要 |
A method is provided for producing a joint member of a metal joint, such that reduction of assembly manhours and reduction of the thickness and weight can be achieved at the same time without reducing the strength of a product or increasing the cost of production. In the case of a nut-side thin joint member, a metal plate of boron steel obtained by adding boron to low-carbon steel is burred such that the resulting cylindrical body obtains a surface that is sufficient for threading, then a threaded portion having a plurality of threads is formed on that surface, after which, quenching is carried out to increase the strength of the threads so that a nut having sufficient strength can be integrally provided even though the thickness and weight of the joint member are reduced. |
申请公布号 |
US9303668(B2) |
申请公布日期 |
2016.04.05 |
申请号 |
US201013504241 |
申请日期 |
2010.10.05 |
申请人 |
KABUSHIKI KAISHA YOSHINO KOSAKUJO |
发明人 |
Yoshino Masahiro |
分类号 |
F16B7/04;B21D28/32;C21D8/02 |
主分类号 |
F16B7/04 |
代理机构 |
Oliff PLC |
代理人 |
Oliff PLC |
主权项 |
1. A method of producing a nut-side thin joint member of a pipe coupling metal joint for coupling two pipes to each other in a manner that the two pipes are held between a circular-arc shaped surface of the nut-side thin joint member and a circular-arc shaped surface of a bolt-side thin joint member, the surfaces each following curved surfaces of the pipes to be held, and fastened by a bolt and a nut, the method comprising:
preparing a thin metal sheet with thickness of 1.0 to 1.3 mm, made of boron steel, the thin metal sheet having 0.20 to 0.25 mass % of carbon and 0.001 to 0.005 mass % of boron; bending the thin metal sheet into a three-dimensionally shaped, pre-joint member having the circular-arc shaped surface; forming a cylindrical body portion in the pre-joint member by performing burring; forming a threaded part having a thread ridge comprising 3 to 3.5 ridges by performing rolling tapping on the cylindrical body, so as to make a nut; and thereafter performing quenching on the pre-joint member, the pre-joint member being heated in a furnace at a temperature of 870° C. to 900° C., thereby forming the nut-side thin joint member with the threaded part, the thickness of the thread ridge being kept 0.8 mm or more. |