Method of synthesis of CMK-3-type carbon replica

摘要

The method of obtaining the CMK-3-type carbon replica, consisting of the introduction of SBA-15-type molecular sieve to a mixture of furfuryl alcohol and a solvent, the subsequent polycondensation of furfuryl alcohol, carbonization of the prepared, composite and removal of the hard template, according to the invention, is characterized in that the reaction of furfuryl alcohol polycondensation is carried out by the precipitation method in a slurry containing SBA-15 silica sieve, water, furfuryl alcohol and concentrated solution of hydrochloric acid in mass ratios, respectively, in the range from 1.00:32.33:1.00:6.65 to 1.00:30.83:2.50:16.64, whereas the ratio of the total mass of furfuryl alcohol and water to the mass of SBA-15 as well as the mass ratio of the concentrated HCl solution to the mass of furfuryl alcohol are kept at the constant value every time.

主权项

1. The method of obtaining the CMK-3-type carbon replica, consisting of the introduction of SBA-15-type silica mesoporous sieve to a mixture of furfuryl alcohol and a solvent, the subsequent polycondensation of furfuryl alcohol, carbonization of the prepared composite and removal of hard template (SIO2), wherein the reaction of furfuryl alcohol polycondensation is carried out by the precipitation method in a slurry containing SBA-15 silica sieve, water, furfuryl alcohol and concentrated solution of hydrochloric acid in mass ratios, respectively, in the range from 1.00:32.33:1.00:6.65 to 1.00:30.83:2.50:16.64, whereas the ratio of the total mass of furfuryl alcohol and water to the mass of SBA-15 as well as the mass ratio of the concentrated HCl solution to the mass of furfuryl alcohol are kept at the constant value for each synthesis.