LOW-TEMPERATURE FAST-FIRED LIGHTWEIGHT CERAMIC HEAT INSULATION PLATE AND PREPARATION METHOD THEREOF

摘要

A low-temperature fast-fired lightweight ceramic heat insulation plate and a preparation method thereof. The preparation method comprises: performing ball milling and powder spraying on a raw material containing foamable ceramic waste slag to prepare foamable powder, the foamable ceramic waste slag accounting for 80-100 wt % of the weight of the raw material; uniformly mixing 100 weight portions of the foamable powder with 3-15 weight portions of granular powder of a low-melting-point organic matter to obtain mixed powder materials; pressing the mixed powder materials under 10-20 MPa to prepare a ceramic green body; and firing the ceramic green body at a temperature of 1100-1170° C. to prepare the lightweight energy-saving ceramic heat insulation plate.

主权项

1. A preparation method of low-temperature fast-fired lightweight ceramic heat insulation plates, comprising:
performing ball milling and powder spraying on raw materials containing foamable ceramic waste to make foamable powders, the weight percentages of the foamable ceramic waste in the raw materials being 80-100 wt %; mixing 100 weight parts of the foamable powders with 3-15 weight parts of granular powders of organics with low melting points uniformly to obtain mixed powder materials, the particle sizes of the foamable powders being 0.18-0.98 mm, and the particle sizes of the organics with low melting points being 0.15-0.25 mm; pressing the mixed powder materials under 10-20 MPa to make a ceramic green body; and firing the ceramic green body at 1100-1170° C. to make the lightweight energy-saving ceramic heat insulation plates, the procedure parameters for the firing being: the ceramic green body is heated to a temperature ranging from 1100° C. to 1170° C. within 20-35 minutes, and kept at the temperature for 5-10 minutes; the organics with low melting points including polyethylene wax and polypropylene wax.