PROBLEM TO BE SOLVED: To provide a polyolefin composition excellent in transparency which hardly causes dropping of an antiblocking agent while maintaining blocking resistance in comparison with conventional one.SOLUTION: There is provided a polyolefin composition comprising the following (a) to (c) components, wherein the content of an olefinic polymer (A) is 0.5 mass% or more and less than 50 mass% based on 100 mass% of the total amount of (a) and (b): (a) an olefinic polymer (A) having a melting endothermic amount (&Dgr;H-D) obtained from a melting endotherm curve which is obtained by retaining a sample in a nitrogen atmosphere at -10°C for 5 minutes and then heating at 10°C/min using a differential scanning calorimeter (DSC) of 0 to 80 J/g and a molecular weight distribution (Mw/Mn) of less than 3.0, (b) an olefinic polymer (B) having a melting point (Tm-D) measured by a differential scanning calorimeter (DSC) of more than 120°C, and (c) an antiblocking agent.SELECTED DRAWING: None |