发明名称 |
METHOD OF MANUFACTURING OF LIGHT CERAMIC PROPPANTS AND LIGHT CERAMIC PROPPANTS |
摘要 |
A method for manufacturing of light ceramic proppants made from a mixture of raw materials that is mechanically granulated in a granulator or that is granulated in a spray dryer from a pourable ceramc mass, to obtain granulate having a granule size of 150-1700 μm (12-100 U.S. Mesh, ASTM E11-04, ISO 13503-2), and next the granulate is fired and the fired granulate is fractioned. The mixture of raw materials is prepared from: illite-beidellite-ka-olinite high-plastic clays of the Poznan series in the amount of 10% to 40% by weight; kaolinite clays in the amount of 10% to 45% by weight; kaolin in the amount of 20% to 40% by weight; fly ash from brown coal combusted in a power plant in the amount of 10% to 35% by weight; and treatment agents in the amount of up to 10% by weight. The mixture of raw materials is mixed and homogenized in a homogenizer, and the obtained granulate is fed to a fluidised bed dryer, in which it is dried to a moisture content below 3%, and the granulate is fired in a rotary furnace in a temperature from 1150° C. up to 1410° C. in time from 120 to 600 min, obtaining proppants which contain from 18% to 32% by weight of Al203, from 40% to 76% by weight of SiO2, and have a specific gravity from 2.15 Mg/m3 to 2.90 Mg/m3 and a bulk density from 1.35 Mg/m3 to 1.70 Mg/m3, depending on the firing time. |
申请公布号 |
US2016053162(A1) |
申请公布日期 |
2016.02.25 |
申请号 |
US201314778613 |
申请日期 |
2013.12.27 |
申请人 |
BALTIC CERAMICS S.A. |
发明人 |
MARCHWICKI MACIEJ |
分类号 |
C09K8/80;C04B35/14 |
主分类号 |
C09K8/80 |
代理机构 |
|
代理人 |
|
主权项 |
1. A method for manufacturing of ceramic proppants, the method comprising:
preparing a mixture of raw materials comprising:
illite-beidellite-kaolinite high-plastic clays of the Poznan series in the amount of 10% to 40% by weight, containing from 10% to 27% by weight of Al2O3;kaolinite clays in the amount of 10% to 45% by weight, containing from 18% to 32% by weight of Al2O3;kaolin in the amount of 20% to 40% by weight, containing from 28% to 40% by weight of Al2O3;fly ash from brown coal combusted in a power plant in the amount of 10% to 35% by weight, containing from 5% to 15% by weight of Al2O3;and treatment agents in the amount of up to 10% by weight; mixing the mixture of the raw materials homogenizing the mixture of the raw materials in a homogenizer to obtain a homogenized mixture, granuting the homogenized mixture to a granulate having a granule size of 12-100 Mesh (ASTM E11-04 ISO 13503-2). drying the granulate in fluidised bed dryer to reduce moisture content below 3%, and firing the granulate in a rotary furnace in a temperature from 1150° C. to 1410° C. for a time from 120 to 600 min, to obtain proppants which contain from 18% to 32% by weight of Al2O3, from 40% to 76% by weight of SiO2, and have a specific gravity from 2.15 Mg/m3 to 2.90 Mg/m3 and a bulk density from 1.35 Mg/m3 to 1.70 Mg/m3, depending on the time of firing. |