Procedure to optimize materials for cathodes and cathode material having enhanced electrochemical properties |
摘要 |
A material C-AxM(XO4)y that is of particles of a compound of the formula AxM(XO4)y, wherein said particles include a carbon deposit deposited by means of pyrolysis on at least a portion of the surface thereof, and where: A is Li alone or partially replaced by at most 10 atomic % of Na or K; M is Fe(II), or Mn(II), or mixtures thereof alone or partially replaced by at most 30 atomic % of one or more metals selected from Mn, Ni and Co and/or at most 5% of Fe(III); XO4 is PO4 alone or partially replaced by at most 10 molar % of at least one group selected from SO4, SiO4 and MoO4; and where said material has a calcium impurity content of lower than about 1000 ppm. |
申请公布号 |
US9269950(B2) |
申请公布日期 |
2016.02.23 |
申请号 |
US201213693908 |
申请日期 |
2012.12.04 |
申请人 |
JOHNSON MATTHEY PUBLIC LIMITED COMPANY;BATHIUM CANADA INC. |
发明人 |
Geoffroy Denis;Liang Guoxian;Gauthier Michel;Lahrs Thorsten;Ravet Nathalie;Parent Michel;Vallee Alain;Leblanc Patrick;Cotton Frederic |
分类号 |
H01M4/136;H01M4/1397;G01N33/20;H01M10/0565;H01M4/36;H01M4/58;C01B25/45;H01M10/052 |
主分类号 |
H01M4/136 |
代理机构 |
Marshall, Gerstein & Borun LLP |
代理人 |
Marshall, Gerstein & Borun LLP |
主权项 |
1. A material C-AxM(XO4)y consisting of particles of a compound with the formula AxM(XO4)y, where the particles comprise a carbon deposit deposited by pyrolysis on at least part of its surface, wherein:
A stands for Li, alone or partially replaced by at most 10% atomic percentage of Na or K; M stands for Fe(II) or Mn(II), or mixtures thereof, alone or partially replaced by at most 30% atomic percentage of the atoms of one or more other metals chosen from Ni and Co, and/or by at most 10% atomic percentage of one or more aliovalent or isovalent metals other than Ni or Co, and/or by at most 5% atomic percentage of Fe(III); and XO4 stands for PO4 alone or partially replaced by at most 10% atomic percentage of at least one group chosen from among SO4, SiO4, and MoO4; and 0<x≦2 and 0<y≦2, the coefficients x and y being chosen independently to ensure electroneutrality of the oxide complex, and wherein the material has a level of calcium present as an impurity lower than approximately 1000 ppm, said calcium being principally deposited on the surface of the material C-AxM(XO4)y. |