Method for producing aluminum foil |
摘要 |
A method for producing an aluminum foil of the present invention is characterized in that an aluminum film is formed on a surface of a substrate by electrolysis using a plating solution containing at least (1) a dialkyl sulfone, (2) an aluminum halide, and (3) at least one nitrogen-containing compound selected from the group consisting of an ammonium halide, a hydrogen halide salt of a primary amine, a hydrogen halide salt of a secondary amine, a hydrogen halide salt of a tertiary amine, and a quaternary ammonium salt represented by the general formula: R1R2R3R4N.X (R1 to R4 independently represent an alkyl group and are the same as or different from one another, and X represents a counteranion for the quaternary ammonium cation), then the film is separated from the substrate to obtain an aluminum foil, and the obtained aluminum foil is subjected to a heat treatment. |
申请公布号 |
US9267216(B2) |
申请公布日期 |
2016.02.23 |
申请号 |
US201113883643 |
申请日期 |
2011.11.10 |
申请人 |
HITACHI METALS LTD. |
发明人 |
Okamoto Atsushi;Hoshi Hiroyuki;Andou Setsuo |
分类号 |
C25D3/44;H01G11/30;H01M4/66;C25D1/04;C25D5/50;C25D7/06;H01G9/00;H01G11/22;H01G11/84;H01M10/052 |
主分类号 |
C25D3/44 |
代理机构 |
Kratz, Quintos & Hanson, LLP |
代理人 |
Kratz, Quintos & Hanson, LLP |
主权项 |
1. A method for producing an aluminum foil, comprising the steps of:
forming an aluminum film on a surface of a substrate by electrolysis using a plating solution containing at least (1) a dialkyl sulfone, (2) an aluminum halide, and (3) a nitrogen-containing compound; separating the film from the substrate to obtain an aluminum foil; and subjecting the obtained foil to a heat treatment, wherein the heat treatment is conducted in an ambient atmosphere, and wherein the ambient atmosphere is at a temperature of 80 to 550° C. |