Polyester resin and method for preparing the same

摘要

There is provided a polyester resin including: moieties of dicarboxylic acid components including terephthalic acid; and moieties of diol components including 5 to 60 mole % of isosorbide, 10 to 80 mole % of a cyclohexanedimethanol, and the balance of other diol compounds, wherein the polyester resin has an intrinsic viscosity of 0.5 to 1.0 dl/g and oxygen permeability of less than 20 cc*mm/(m2*day*atm), as measured by ASTM D 3985, and There is also provided a method for preparing the polyester resin, including: esterifying diol components including 5 to 60 mole % of isosorbide, 10 to 80 mole % of a cyclohexanedimethanol, and the balance of other diol compounds, with dicarboxylic acid components including terephthalic acid in the presence of an esterification reaction catalyst including a zinc compound; adding a phosphorus-based stabilizer to the esterification reaction mixture at the time when the degree of esterification reaches at least 80%; and subjecting the esterification reaction product to polycondensation.

主权项

1. A polyester resin comprising:
moieties of dicarboxylic acid components comprising terephthalic acid; and moieties of diol components comprising 5 to 60 mole % of isosorbide, 10 to 80 mole % of a cyclohexanedimethanol, and the balance of other diol compounds, wherein the polyester resin has an intrinsic viscosity of 0.5 to 1.0 dl/g, and oxygen permeability of less than 20 cc*mm/(m2*day*atm), as measured by ASTM D 3985, and wherein the polyester resin contains 1 to 100 ppm of a zinc-based catalyst, in terms of the central metal atom content, based on the total amount of the resin, and 10 ppm to 300 ppm of a phosphorus-based stabilizer.