The present invention relates to a method for manufacturing fabric with superior material properties including the following steps: preparing fabric; coating the fabric with a coating composition containing 100 parts by weight of resin, 20 ± 2 parts by weight of methyl ethyl ketone, 30 ± 2 parts by weight of dimethylformamide, 2 ± 1 parts by weight of slip agent, 5 ± 1 parts by weight of antistatic agent, 3 ± 0.5 parts by weight of matting agent, 10 ± 0.5 parts by weight of curing agent, and 0.2 ± 0.05 parts by weight of curing accelerator; and drying the coated fabric by passing the coated fabric through a first drying chamber at 80 ± 3°C, a second drying chamber at 120 ± 3°C, a third drying chamber at 150 ± 3°C, and a fourth drying chamber at 110 ± 3°C at a line speed of 13 ± 0.5 m/min. |