Provided is a molded article having a shape that produces a light-focusing or light-scattering effect, the molded article having exceptional mechanical strength and heat resistance and a high thickness deviation ratio. This molded article is a cured product of a curable composition containing an epoxy compound (A), wherein the molded article comprises a cured article having a flexural modulus (measured in accordance with JIS K7171 (2008), using a test piece (20 mm long, 2.5 mm wide, and 0.5 mm thick) at a support point distance of 16 mm) of 2.5 GPa or greater, the molded article having a thickness deviation ratio (thickness at thickest portion/thickness at thinnest portion) of 5 or greater and exhibiting a light-focusing or light-scattering effect. This molded article preferably has thickness of 0.2 mm or less at the thinnest portion thereof. The curable composition is preferably a photocurable composition. |