发明名称 |
Refined white ceramic material and method for preparing same |
摘要 |
Disclosed is a refined white ceramic material, which belongs to the field of ceramic materials for component packaging, and comprises the following raw materials by weight in percentage: aluminum oxide 87-93, magnesium oxide 0.8-5, silicon dioxide 1-6, calcium oxide 0.6-4, titanium dioxide 0.01-0.5, and zirconium dioxide 0.5-3. The method for preparing same comprises: (1) washing aluminum oxide grinding balls and a ball-milling tank, and drying for later use; (2) weighing a solvent NP-10 of 0.5-4 by weight in percentage, and adding the solvent into the ball-milling tank; (3) weighing raw materials, adding the raw materials into the ball-milling tank, and performing ball milling for 72±0.5 h. By means of the refined white ceramic material of the present invention, the obtained ceramic grains have even sizes, small surface roughness, and high fracture resistance performance of ceramic body. |
申请公布号 |
US9242901(B2) |
申请公布日期 |
2016.01.26 |
申请号 |
US201214127883 |
申请日期 |
2012.02.17 |
申请人 |
THE 13TH RESEARCH INSTITUTE OF CHINA ELECTRONICS TECHNOLOGY GROUP CORPORATION |
发明人 |
Zheng Hongyu;Shi Pengyuan;Jin Huajiang;Ren Caihua;Zhang Bingqu;Zhang Jinli |
分类号 |
C04B35/119;C04B35/111;C04B35/626;C04B35/634 |
主分类号 |
C04B35/119 |
代理机构 |
Hamre, Schumann, Mueller & Larson, P.C. |
代理人 |
Hamre, Schumann, Mueller & Larson, P.C. |
主权项 |
1. A method for producing a refined white ceramic material, comprising the steps of:
(1) cleaning the alumina grinding balls and ball mill jar, and drying the balls and the mill jar for later use; (2) weighing 0.5-4 parts by weight of nonylphenol polyoxyethylene ether as a solvent, and adding the solvent into the ball mill jar; (3) weighing the following raw materials in parts by weight: 87-93 parts of aluminum oxide, 0.8-5 parts of magnesium oxide, 1-6 parts of silicon dioxide, 0.6-4 parts of calcium oxide, 0.01-0.5 parts of titanium dioxide and 0.5-3 parts of zirconium dioxide, and adding the raw materials into the ball mill jar, performing ball grinding for 72±0.5 h. |