| 摘要 |
Disclosed is a high filling and high resilience soft foaming polyethylene material, comprising the following parts of raw materials by weight: 15-20 parts polyethylene, 5-20 parts elastomers, 60-80 parts modified calcium carbonate, 1-10 parts chemical foaming agent, 0.5-1.5 5 parts crosslinking agent and 1-5 parts physical foaming agent. Also disclosed is a method of preparing high filling and high resilience soft foaming polyethylene material. The present invention can prepare a high calcium carbonate filling and high resilience soft foaming polyethylene material with calcium carbonate filler content as high as 55-75%, improving rigidity, hardness and compressive strength of the material while maintaining the elasticity of 0 the foaming material, and reducing material density. The present invention has a simple process, greatly reduces costs and is economical and practical. |