| 摘要 |
The present invention provides a Ni-based single crystal superalloy which has the following composition by weight: 0.1 wt % or more and 9.9 wt % or less of Co, 5.1 wt % or more and 10.0 wt % or less of Cr, 1.0 wt % or more and 4.0 wt % or less of Mo, 8.1 wt % or more and 11.0 wt % or less of W, 4.0 wt % or more and 9.0 wt % or less of Ta, 5.2 wt % or more and 7.0 wt % or less of Al, 0.1 wt % or more and 2.0 wt % or less of Ti, 0.05 wt % or more and 0.3 wt % or less of Hf, 1.0 wt % or less of Nb and less than 3.0 wt % of Re with the remainder including Ni and unavoidable impurities. This Ni-based single crystal superalloy has a low Re content and also has excellent high-temperature strength, mainly creep strength. |
| 主权项 |
1. A method of manufacturing a Ni-based single crystal superalloy which has the following composition by weight: 0.1 wt % or more and 9.9 wt % or less of Co, 5.1 wt % or more and 10.0 wt % or less of Cr, 1.0 wt % or more and 4.0 wt % or less of Mo, 8.1 wt % or more and 11.0 wt % or less of W, 4.0 wt % or more and 9.0 wt % or less of Ta, 5.2 wt % or more and 7.0 wt % or less of Al, 1.1 wt % or more and 2.0 wt % or less of Ti, 0.05 wt % or more and 0.3 wt % or less of Hf, 1.0 wt % or less of Nb and 0.8 wt % or less of Re with the remainder including Ni and unavoidable impurities,
wherein the Ni-based single crystal superalloy is obtained by performing a solution heat treatment and an aging treatment to an alloy ingot which has the above-described composition, and wherein the solution heat treatment is carried out by raising the ingot from a temperature within a range of 1,503 to 1,563 K (1,230 to 1,290° C.) to a temperature within a range of 1,573 to 1,613 K (1,300 to 1340° C.) by a multi-stage step, followed by maintaining of such a temperature for 1 hour or more; and the aging treatment is carried out by performing a primary aging treatment of maintaining the ingot at a temperature within a range of 1,273 to 1,423 K (1,000° C. to 1,150° C.) for 3 to 5 hours and by performing a secondary aging treatment of maintaining the ingot at a temperature within a range of 1,073 to 1,223 K (800° C. to 950° C.) for 15 to 25 hours. |