High strength, hot dipped galvanized steel sheet excellent in shapeability and method of production of same

摘要

A high strength hot dipped galvanized steel sheet is provided. By controlling the amount of addition of Ti instead of the addition of Nb or B, it is possible to obtain an effect of retarding recrystallization and grain growth even if annealing by a continuous annealing process in a temperature range of the general annealing temperature of 720° C. to a temperature of the lower of 800° C. or Ac3 temperature. By controlling the rolling and heat treatment conditions, it is possible to control the ferrite phase rate, grain size of the low temperature transformed phases, ratio of average values of the nano hardnesses of the ferrite phase and low temperature transformed phases, and fluctuations of hardnesses of the low temperature transformed phases in a composite structure steel of ferrite and low temperature transformed phases and obtain a high strength hot dipped galvanized steel sheet.

主权项

1. A method of production of high strength hot dipped galvanized steel sheet having an average grain size of a low temperature transformed phase of 0.1 to 1 μm, a ratio of average nano hardnesses of a ferrite phase and the low temperature transformed phase of 1.5 to 3.0, and a nano hardness of the low temperature transformed phase at 80% or more of the measurement points of 1 to 5 times the average nano hardness of the ferrite phase, the method comprising:
heating a slab to 1000 to 1350° C., the slab having steel ingredients, by mass %, C: 0.05 to 0.1%, Si: 0.1 to 1.0%, Mn: 2.0% to 2.5%, Al: 0.02 to 0.1%, Ti: 0.01 to 0.05%, Cr: 0.1 to 1.0%, Sn: 0.0010 to 0.1%, and a balance of Fe and unavoidable impurities, as the unavoidable impurities, P: 0.03% or less, S: 0.01% or less, Nb: 0.001% or less, V: 0.001% or less, W: 0.001% or less, Mo: 0.001% or less, Zr: 0.001% or less, B: 0.0001% or less, then hot rolling at a final rolling temperature Ar3 or more, coiling at 600° C. or less, pickling, cold rolling at a rolling rate of 30 to 70% and a draft per pass of 30% or less, annealing at a temperature in the range of 720° C. to the lower of 850° C. or an Ac3 temperature, wherein a heating rate from at least 600° C. to an annealing temperature is 0.5-6° C./sec, holding at the annealing temperature for 10 sec or more, then cooling in at least the temperature range of the annealing temperature to 650° C. by a cooling rate of 5° C./sec or more, further cooling in at least the temperature range of 600° C. to 500° C. by a cooling rate of 3° C./sec or less, and then performing hot dip galvanization or hot dip galvannealization.