Ti(C,N)-based cermet with Ni3Al and Ni as binder and preparation method thereof

摘要

Provided are Ti(C,N)-based cermets with Ni3Al and Ni as binder and a preparation method thereof. The Ti(C,N)-based cermets are prepared by raw materials subjected to ball-mill mixing, die forming, vacuum degreasing and vacuum sintering, wherein weight percentage of each chemical component of the raw materials is as follows: TiC 34.2˜43%, TiN 8˜15%, Mo 10˜15%, WC 5˜10%, graphite 0.8˜1.0%, Ni 20˜24%, and Ni3Al powder containing B 6˜10%. Ni powder and Ni3Al powder containing B are used as binder. The Ti(C,N)-based cermets feature in excellent corrosion resistance, oxidation resistance and mechanical properties at high temperature, has a hardness of 89.0˜91.9 HRA, a room temperature bending strength of 1600 MPa or more, and a fracture toughness of 14 MPa·m1/2 or more, and is applicable for manufacturing high-speed cutting tools, dies and heat-resisting and corrosion-resisting components.

主权项

1. A Ti(C,N)-based cermet with Ni3Al and Ni as binder materials, prepared by subjecting raw materials to ball-mill mixing, die forming, vacuum degreasing, and vacuum sintering, wherein:
raw materials for preparing the cermets comprise TiC, TiN, Mo, WC, graphite, Ni powder, and Ni3Al powder containing B, wherein each component of the raw materials has a weight percentage as follows: TiC 34.2-43%, TiN 8-15%, Mo 10-15%, WC 5-10%, graphite 0.8 -1.0%, Ni powder 20-24%, and Ni3Al powder containing B 6-10%; and each element of the Ni3Al powder containing B has a weight percentage as follows: Ni 87.23-88.48%, Al 11.47-12.68%, and B 0.5-1.0%.