| 摘要 |
PROBLEM TO BE SOLVED: To provide a polyethylene resin composition for container excellent in environmental stress crack resistance and shock resistance and capable of being molded with thicker and light amount, high in crystallization kinetic, excellent in high speed moldability and capable of making molding high cycle and a molded body containing the same.SOLUTION: There is provided a polyethylene resin composition for container polymerized to polyethylene (I) of 60 to 90 wt.% by using a metallocene catalyst containing Ti, Zr or Hf, having melt flow rate (HLMFR) at temperature of 190°C and load of 21.6 Kg of 0.2 g/10 min. or more and less than 5 g/10 min. and density of 0.915 to 0.945 g/cmand containing an ethylene polymer (II) having a long chain branch structure of 10 to 40 wt.% and satisfying specific properties. |