| 摘要 |
An iron-chromium based brazing filler metal is provided which exhibits an excellent wetting behavior on a stainless steel base material. The brazing filler metal produces a brazed joint which exhibits high strength and good corrosion resistance. The brazing filler metal is suitable for brazing stainless steel and other materials where corrosion resistance and high strength is required. Typical examples of applications are heat exchangers and catalytic converters. The iron-chromium based brazing filler metal powder according to the invention comprises: between 11 and 35 wt % chromium, between 0 and 30 wt % nickel, between 2 and 20 wt % copper, between 2 and 6 wt % silicon, between 4 and 8 wt % phosporous, between 0-10 wt % manganese, and at least 20 wt % iron. |