The present invention provides a high-strength hot-rolled steel sheet having both excellent strength and excellent workability (particularly, bending workability), and a method of producing the same.;The steel sheet of the present invention has a certain composition as well as microstructures such that an area ratio of ferrite phase is 95% or more, an average grain size of the ferrite phase is 8 μm or less, and carbides in grains of the ferrite phase have an average particle size of less than 10 nm. The steel sheet of the present invention also has a tensile strength of 980 MPa or more. |