Metal matrix ceramic composite and manufacturing method and application thereof

摘要

A metal matrix ceramic composite is completely formed by permeating at least part of a matrix metal into an array of ceramic granules by squeeze-casting, and the volume percentage of the ceramic granules may be adjusted within a range of 10%-80% of the metal matrix ceramic composite according to the usage requirements. The metal matrix ceramic composites not only retain high performance of anti-penetration, but also have the strong toughness of the metal; in addition, this composite has features of low density, resistance against ordinary mechanical cutting and flame cutting, and inhibition of crack propagation and the like. The composite has broad application prospects in the protection of such important security facilities as safes, automatic teller machines and vault gates.

主权项

1. A method for manufacturing a metal matrix ceramic composite comprising steps of:
heating ceramic granules and maintaining a heating temperature of the ceramic granules between 400° C. and 1400° C. according to type of matrix metals and ceramics used, wherein the heating temperature of the ceramic granules depends on type of ceramics and matrix metals, and the heating temperature of the ceramic granules is in a range of 300° C. below to 200° C. above a melting point of the matrix metals and the ceramic granules have a diameter between 3 mm and 9 mm; transferring the heated ceramic granules in a multi-layer arrangement into a cavity of a squeeze-casting mold; performing compaction; pouring molten metal matrix into the cavity of the mold; pressurizing and maintaining a pressure, based on material of the metal matrix, type of ceramic granules, and a desired product structure and specification; adjusting the pressure between 50 MPa and 200 MPa based on material of the metal matrix, type of ceramic granules, and the desired product structure and specification; maintaining the pressure for a time between 30 s and 5 min; and removing the metal matrix ceramic composite out from the mold; wherein the metal matrix ceramic composite having a thickness of above 20 mm can resist against oxyacetylene cutting for more than 30 min without piercing.