发明名称 |
Injection-molded reactor and compound used in same |
摘要 |
[Problem] Provided is an injection-molded reactor which has a further reduced loss when the reactor is in operation.;[Solution Means] The injection-molded reactor is configured by injection-molding a core using a compound for a core so that a coil obtained by winding a electric wire is embedded in the core without leaving any space therein, the compound being a compound obtained by adding a low-melting-point resin B that has a melting point of 150° C. or lower to a base resin A that is a highly heat-resistant resin with a melting point of 150° C. or higher and that accounts for most of thermoplastic resins forming a resin binder, the melting point of the low-melting-point resin B being lower than that of the base resin A, and mixing the base resin A and the low-melting-point resin B as the thermoplastic resins with a soft magnetic powder in a proportion represented by the following expression (1):
X·(soft magnetic powder)+(100−X)·((100−Y)·(base resin A)+Y·(low-melting-point resin B)) expression (1)whereinX is 83-96% by mass andY is 2-40% by mass. |
申请公布号 |
US9202618(B2) |
申请公布日期 |
2015.12.01 |
申请号 |
US201214351533 |
申请日期 |
2012.09.19 |
申请人 |
DAIDO STEEL CO., LTD. |
发明人 |
Esaki Junichi;Tozawa Yusuke;Kajinami Yoshitomo;Yoshimoto Kousuke |
分类号 |
H01F27/02;H01F27/255;H01F1/26;H01F37/00;B29C45/00;H01F41/12;H01F1/147;H01F27/22;H01F27/28;B29C45/14;B29C45/16;H01F17/04 |
主分类号 |
H01F27/02 |
代理机构 |
McGinn IP Law Group, PLLC. |
代理人 |
McGinn IP Law Group, PLLC. |
主权项 |
1. An injection-molded reactor, wherein a substance obtained by adding a low-melting-point resin B that has a melting point of 150° C. or lower and has a lower melting point than that of a base resin A to the base resin A that is a highly heat-resistant resin with a melting point of 150° C. or higher and that accounts for most of a thermoplastic resin is used as the thermoplastic resin forming a resin binder; a compound for a core is obtained by mixing the base resin A and the low-melting-point resin B with a soft magnetic powder in a proportion represented by the following expression (1); and the core is injection-molded by using the compound in a state where a coil in which a electric wire is wound is embedded in an inner portion without an interval to configure the injection-molded reactor,
X·(soft magnetic powder)+(100−X)·((100−Y)·(base resin A)+Y·(low-melting-point resin B)) expression (1) wherein X is 83 to 96% by mass and Y is 2 to 40% by mass. |