发明名称 |
Surface-treatment solution for zinc or zinc alloy coated steel sheet and method for manufacturing zinc or zinc alloy coated steel sheet |
摘要 |
A zinc or zinc alloy coated steel sheet has a surface-treatment film formed thereon in a coating weight per one surface of 100 to 600 mg/m2. The surface-treatment film is obtained by applying, onto a surface of the zinc or zinc alloy coated steel sheet, the surface-treatment solution prepared by mixing the following components at specific ratios, the surface-treatment solution having pH of 8 to 10: a silane compound (A) having a hydrolyzable group, obtained from a silane coupling agent (a1) having a glycidyl group, a tetraalkoxysilane (a2), and a chelating agent (a3); a zirconium carbonate compound (B); a vanadate compound (C); a nitric compound (D); and water, and by subsequently heating and drying the surface-treatment solution thus applied. |
申请公布号 |
US9187829(B2) |
申请公布日期 |
2015.11.17 |
申请号 |
US201214344140 |
申请日期 |
2012.09.12 |
申请人 |
JFE Steel Corporation |
发明人 |
Kaneko Rie;Matsuda Takeshi;Matsuzaki Akira;Oshima Yasuhide |
分类号 |
C23C22/62;C23C22/74;B32B15/04;B32B15/18;B05D3/00;C09D5/08;B05D3/02;C23C22/60 |
主分类号 |
C23C22/62 |
代理机构 |
DLA Piper LLP (US) |
代理人 |
DLA Piper LLP (US) |
主权项 |
1. A surface-treatment solution for a zinc or zinc alloy coated steel sheet, comprising:
a silane compound (A) having a hydrolyzable group, the silane compound (A) being obtained from a silane coupling agent (a1) having a glycidyl group, a tetraalkoxysilane (a2), and a chelating agent (a3); a zirconium carbonate compound (B); a vanadate compound (C); a nitrate compound (D) selected from the group consisting of at least one of ammonium salt and alkali metal salt; and water, and satisfying (I) to (IV) below, the surface treatment solution having pH of 8 to 10, wherein (I) to (IV) are as follows: (I) content of the silane compound (A) with respect to total solid content of the surface-treatment solution is 30 to 70 mass %; (II) mass ratio (B/A) of the ZrO2-equivalent mass of the zirconium carbonate compound (B) with respect to the content of the silane compound (A) is 0.3 to 2.0; (III) mass ratio (C/A) of the V-equivalent mass of the vanadate compound (C) with respect to the content of the silane compound (A) is 0.01 to 0.15; and (IV) mass ratio (D/A) of the content of the nitrate compound (D) with respect to the content of the silane compound (A) is 0.005 to 0.08. |
地址 |
JP |