发明名称 |
Ferric phosphate and methods of preparation thereof |
摘要 |
High-purity crystalline ferric phosphate material with desirable characteristics for use in synthesis of nano-sized LFP cathode material are described. The ferric phosphate dihydrate material has as disclosed herein has a molar ratio of phosphorous to iron is from about 1.001 to about 1.05, a surface area of from about 25 m2/g to about 65 m2/g, and is substantially free of metallic or magnetic impurities. Methods of synthesizing high-purity crystalline ferric phosphate material with desirable characteristics for use in synthesis of nano-sized LFP cathode material are also described. In some embodiments, one or more magnetic traps are used during the reaction process and/or after the formation of the final product to remove magnetic impurities. In some embodiments, a synthetic method of ferric phosphate using multiple steps is described, wherein the intermediate of the synthesis is isolated and purified to improve the purity of the ferric phosphate material. In some embodiments, an iron compound is added to an aqueous solution of phosphoric acid. The solution pH and temperature are controlled to ensure the complete dissolution of the iron compound. The desired iron phosphate crystalline material can be obtained with high purity and high crystalline phase purity by controlling the pH and temperature of the solution. |
申请公布号 |
US9174846(B2) |
申请公布日期 |
2015.11.03 |
申请号 |
US201012885907 |
申请日期 |
2010.09.20 |
申请人 |
A123 Systems LLC |
发明人 |
Beck Larry W.;Soltani Mahrokh;Wang Liya |
分类号 |
C01B15/16;C01B25/26;C01G1/00;C01G49/00;C01G51/00;C01G53/00;C22B1/00;C22B23/00;C01B25/37;H01M4/136;H01M4/58;H01M10/052 |
主分类号 |
C01B15/16 |
代理机构 |
Alleman Hall McCoy Russell & Tuttle LLP |
代理人 |
Alleman Hall McCoy Russell & Tuttle LLP |
主权项 |
1. A method of synthesizing crystalline ferric phosphate material, comprising:
a) introducing an iron (II) salt and a phosphate salt and ammonium hydroxide into an aqueous solution to form a ferrous phosphate material; b) collecting and washing the ferrous phosphate material to remove impurities; and c) after washing the ferrous phosphate, oxidizing the ferrous phosphate from step b) with an oxidizing agent to form a crystalline ferric phosphate material comprising a molar ratio of phosphorus to iron is from about 1.001 to about 1.05; wherein step c) further comprises heating ferrous phosphate at a temperature of between about 35 to about 65° C.; and wherein the crystalline ferric phosphate material comprises less than 100 ppm metallic or magnetic impurities and less than 700 ppm sulfate impurities. |