Liquid crystalline polyester fiber and process for production of the same

摘要

A liquid crystalline polyester fiber which exhibits a half width of endothermic peak (Tm1) of 15° C. or above as observed in differential calorimetry under heating from 50° C. at a temperature elevation rate of 20° C./min and a strength of 12.0 cN/dtex or more; and a process for production of the same. A liquid crystalline polyester fiber which is excellent in abrasion resistance and lengthwise uniformity and is improved in weavability and quality of fabric and which is characterized by a small single-fiber fineness can be efficiently produced without impairing the characteristics inherent in fabric made of liquid crystalline polyester fiber produced by solid phase polymerization, namely, high strength, high elastic modulus and excellent thermal resistance.

主权项

1. A liquid crystalline polyester fiber, wherein said fiber comprises a liquid crystalline polyester comprising the following structural units (I), (II), (III), (IV) and (V), and satisfies the following conditions 1 to 4: Condition 1: weight average molecular weight of the liquid crystalline polyester fiber determined through a polystyrene-equivalent weight average molecular weight is in a range of 250,000 or more and 1,500,000 or less; Condition 2: heat of melting (ΔHm1) of the liquid crystalline polyester fiber, at an endothermic peak (Tm1) observed when measured under a condition of heating from 50° C. at a temperature elevation rate of 20° C./min in differential calorimetry, is 5.0 J/g or more; Condition 3: single-fiber fineness of the liquid crystalline polyester fiber is 18.0 dtex or less; and Condition 4: strength of the liquid crystalline polyester fiber is 13.0 cN/dtex or more.