STEEL SHEET FOR THREE-PIECE CAN AND METHOD FOR MANUFACTURING THE SAME |
摘要 |
Provided are a steel sheet for a can having high buckling strength for a can body against an external force and excellent formability when being formed into a shape having a design effect by additionally giving elongation strain in the circumferential direction after the steel sheet having been formed into a cylindrical shape and a method for manufacturing the steel sheet. The chemical composition is controlled to contain, by mass %, C: 0.0005% or more and 0.0035% or less, Si: 0.050% or less, Mn: more than 0.60% and 1.00% or less, P: 0.030% or less, S: 0.020% or less, Al: 0.010% or more and 0.100% or less, N: 0.0030% or less, B: 0.0005% or more, and the balance being Fe and inevitable impurities, in which the relationship B/N≧0.50 is satisfied where B/N represents;(B(mass %)/10.81)/(N(mass %)/14.01), and a Young's modulus in a direction at an angle of 90° to the rolling direction is 220 GPa or more. |
申请公布号 |
US2015299828(A1) |
申请公布日期 |
2015.10.22 |
申请号 |
US201314440779 |
申请日期 |
2013.11.06 |
申请人 |
JEF STEEL CORPORATION |
发明人 |
Suto Mikito;Kojima Katsumi;Tada Masaki;Nakamaru Hiroki |
分类号 |
C22C38/06;C21D9/46;C22C38/00;C22C38/04;C22C38/02;C21D8/02;C21D6/00 |
主分类号 |
C22C38/06 |
代理机构 |
|
代理人 |
|
主权项 |
1. A steel sheet for a three-piece can, the steel sheet having a chemical composition containing, by mass %, C: 0.0005% or more and 0.0035% or less, Si: 0.050% or less, Mn:
more than 0.60% and 1.00% or less, P: 0.030% or less, S: 0.020% or less, Al: 0.010% or more and 0.100% or less, N: 0.0030% or less, B: 0.0005% or more, and the balance being Fe and inevitable impurities, wherein: the relationship B/N≧0.50 is satisfied (where B/N represents (B(mass %/10.81)/(N(mass %)/14.01)); and a Young's modulus in a direction at an angle of 90° to the rolling direction is 220 GPa or more. |