发明名称 |
METHOD FOR MANUFACTURING GLASS PLATE WITH WHICH WARPING DURING CHEMICAL STRENGTHENING IS REDUCED AND GLASS PLATE |
摘要 |
The present invention relates to a method for producing a float glass sheet, containing a step of melting a glass source material, a step of forming the glass melted in the previous step into a glass ribbon while allowing it to float on a molten metal, and a step of annealing the glass ribbon, in which the float glass sheet is a soda lime silicate glass, and in the forming step, a top surface of the glass ribbon that is opposite to a bottom surface thereof to be in contact with the molten metal is subjected to a dealkalization treatment in the float bath for 1 to 30 seconds and a surface temperature of the glass ribbon during the dealkalization treatment is 600° C. or higher. |
申请公布号 |
US2015291467(A1) |
申请公布日期 |
2015.10.15 |
申请号 |
US201514751321 |
申请日期 |
2015.06.26 |
申请人 |
ASAHI GLASS COMPANY, LIMITED |
发明人 |
MIURA Takenori;SUZUKI Yuichi;IKAWA Nobuaki;KADOKURA Hokuto;YASUDA Kohei |
分类号 |
C03B18/20;C03B18/18;C03C3/087;C03C21/00 |
主分类号 |
C03B18/20 |
代理机构 |
|
代理人 |
|
主权项 |
1. A method for producing a glass sheet, which is a method for producing a float glass sheet, comprising a step of melting a glass source material, a step of forming the glass melted in the previous step into a glass ribbon while allowing it to float on a molten metal, and a step of annealing the glass ribbon, wherein:
the float glass sheet contains (mol %) from 63 to 73% of SiO2, from 0.1 to 5.2% of Al2O3, from 10 to 16% of Na2O, from 0 to 1.5% of K2O, from 5 to 13% of MgO, and from 4 to 10% of CaO, and in the forming step, a top surface of the glass ribbon that is opposite to a bottom surface thereof to be in contact with the molten metal is subjected to a dealkalization treatment in the float bath for 1 to 30 seconds and a surface temperature of the glass ribbon during the dealkalization treatment is 600° C. or higher. |