The present invention relates to colorful regenerated asphalt-concrete and to a method for manufacturing same. More particularly, disclosed are colorful regenerated asphalt-concrete using recycled aggregates from waste asphalt and to a method for manufacturing same, in which products obtained from the thermal decomposition of waste asphalt are mixed with new aggregates and asphalt, and a pigment and an ultraviolet-ray blocker are mixed into the mixture, to thereby not only improve the physical properties of the regenerated asphalt concrete, but also maintain the color of the regenerated asphalt concrete over a long period of time, thus achieving improved weather resistance and durability. |
| 主权项 |
1. A method of manufacturing discoloration-resistant colored regenerated asphalt concrete using recycled aggregate from waste asphalt concrete, comprising: subjecting waste asphalt concrete to grinding to less than 13 mm and heating to 130° C. to 150° C.; mixing the ground waste asphalt concrete, a resin oil composition containing an antioxidant, a pigment and a UV blocker to obtain a waste asphalt concrete mixture, the resin oil composition is used in an amount of 5 wt % to 30 wt %, the pigment is used in an amount of 0.5 wt % to 3 wt %, and the UV blocker is used in an amount of 0.5 wt % to 5 wt %, and the antioxidant is phenyl-beta-naphthylamine, and the resin oil composition comprises 35 wt % to 70 wt % of Vacuum High boiling point Gas Oil (VHGO), 20 wt % to 40 wt % of aromatic base oil, 10 wt % to 30 wt % of paraffin base oil, and 0.3 wt % to 1 wt % of the antioxidant; and mixing the waste asphalt concrete mixture with 30 wt % to 70 wt % of a novel asphalt concrete mixture based on a total weight thereof,
wherein the novel asphalt concrete mixture is composed of 50 wt % of aggregate having a size of 8 mm or less, 38 wt % of aggregate having a size of 8-13 mm, 5-8 wt % of asphalt, and 4-7 wt % of a filler. |