Composite articles are prepared by a spray up operation. In a first step, a gel coat is applied onto a mold surface which has been optionally pretreated with a mold release coating. Next, a barrier coat is applied over the gel coat in the mold and thereafter a laminate formula is applied over the barrier coat. The laminate contains from 40-80% by weight paste and from 20-60% by weight reinforcing fibers. In a preferred embodiment, the paste comprises 90% or more by weight resin, up to 10% filler, and an initiator composition capable of initiating cure at a temperature of 50° C. or lower. In a preferred embodiment, the multilayer composite has a thickness of about 15 mm or less, and is useful as an automobile body panel. The laminate preferably comprises a low shrink, low density glass fiber filled polyester resin. In a preferred embodiment, the paste of the laminate contains a dicyclopentadiene unsaturated polyester resin, polymeric hollow microspheres, and an initiator capable of initiating curing at room temperature or at temperature of 50° C. or less.
|