| 摘要 |
Zirconia sintered bodies containing Y 2 O 3 in solution as a stabilizer have high strength and high toughness and are hence expected to be used as mechanical or structural materials and dental materials. However, no sintered body has been obtained which satisfies both high strength and aesthetic properties based on translucency. The invention relates to the use of a sintered body obtained by subjecting a primary sintered body having a relative density of 95% or higher produced from a fine yttria-containing zirconia powder to HIP sintering at a temperature of 1,200-1,600°C and a pressure of 50 MPa or higher. This sintered body is either a sintered body which has a total light transmittance, as measured at a thickness of 0.5 mm, of 43% or higher and a three-point bending strength of 1,700 MPa or higher or a zirconia sintered body which has a total light transmittance, as measured at a thickness of 1 mm, of 40% or higher and a three-point bending strength of 500 MPa or higher and which combines high strength and total light transmission. |