The invention relates to a dispersion of antimony or indium doped tinoxide nanoparticles in an organic solvent, comprising a) 5-75 wt % of nanoparticles having a mean average size between 1 and 100 nm. b) a solvent comprising a hydroxyl group and an ether group. c) a water content of less then 15 wt %. d) a dispersant content of less then 0.1 wt %. The invention also relates to a method of making such a dispersion, by I. Making a mixture of an aqueous dispersion of antimony or indium doped tinoxide particles having an average size between 1 and 100 nm, a solvent comprising a hydroxyl group and an ether group, which forms an azeotrope with water, and a grafting compound. II. Heating the mixture under stirring at a temperature between 20 and 150° C. III. At least partially removing the solvent/water mixture. IV. Optionally adding more solvent. V. Repeating steps III and IV till the water content of the obtained dispersion is less then a desired value and the concentration solid is between 5 and 70 wt %.
|