A positive electrode active material for a lithium secondary battery containing a lithium-cobalt composite oxide is produced by firing, as a cobalt source, a mixture of substantially spherical cobalt hydroxide or tricobalt tetraoxide having such a sharp particle size distribution that the average particle size D50 is from 7 to 20 μm, and cobalt oxyhydroxide having an average particle size of secondary particles formed by agglomeration of primary particles of from 7 to 20 μm, in a proportion of from 5:1 to 1:5 as the cobalt atomic ratio, at a temperature of from 700° C. to 1050° C. in an oxygen-comprising atmosphere.
|